The photopolymers used in Multi-jet Printing may be hazardous if handled improperly. Repeated skin contact with materials may cause sensitization. Consult the manufacturer’s Global Harmonized Standards/Safety Data Sheet (GHS/SDS) for information on specific materials. For further information on this and related topics, consult the 3D Systems – Materials website at http://www.3dsystems.com/support/materials/msds.
Material Property |
VisiJet® M2R-CL |
VisiJet® M2R-WT |
VisiJet® M2R-BK |
VisiJet® M2R-TN |
VisiJet® M2R-GRY |
VisiJet® M2G-CL |
VisiJet® M2G-DUR |
VisiJet® M2S-HT90 |
VisiJet® M2-EBK |
VisiJet® M2-ENT |
Standard Procedure |
Heat Deflection Temperature (HDT @ 66psi) |
51°C | 51°C | 61°C | 71°C | 51°C | 47°C | N/A | 90°C to 100°C | N/A | N/A | D648 |
Moisture Resistance (absorption) | 0.50% | 0.50% | 0.50% | 0.50% | 0.50% | 0.5% | 0.6% | 0.5% | 0.60% | 0.90% |
D570 |
High Clarity | * * * * * | N/A | N/A | N/A | N/A | * * * * * | * * * * * | * * * | N/A | * * * | N/A |
Stiffness (Shore D Hardness) |
77 | 77 | 81 | 81 | 77 | 70 | 60 | 77 to 84 | N/A | N/A | Hardness Shore D |
Elongation | 20-30 % | 20-30 % | 6-12% | N/A | 20-30 % | 55-65% | 65-75% | 4% to 9% | 160-230% | 160-230% |
D638 |
Impact Strength | 20-25 J/m | 20-25 J/m | 15-18 J/m | N/A | 20-25 J/m | 40-50 J/m | 70-80 J/m | 14 to 17 J/m | N/A | N/A | D256 |
Opacity | N/A | * * * * * | * * * * * | * * * * * | * * * * * | N/A | N/A | N/A | ***** | * * * | N/A |
Color | Transparent Clear | Opaque White | Opaque Black |
Opaque Tan |
Opaque Gray | Transparent Clear | Transparent Clear |
Transparent Clear |
Black |
Amber Translucent |
N/A |
Simulant Characteristics |
VisiJet® M2R-CL |
VisiJet® M2R-WT |
VisiJet® M2R-BK |
VisiJet® M2R-TN |
VisiJet® M2R-GRY |
VisiJet® M2G-CL |
VisiJet® M2G-DUR |
VisiJet® M2S-HT90 |
VisiJet® M2- EBK |
VisiJet® M2- ENT |
|
Polypropylene | * * * | * * * | N/A | N/A | * * * | * * * * | * * * * * | * * * | N/A | N/A | |
ABS | * * * * | * * * * | * * * * | * * * * | * * * * | * * * * * | * * * | * * * * | N/A | N/A | |
Polycarbonate | * * * | N/A | N/A | N/A | N/A | * * * * | N/A | * * * | N/A | N/A | |
Elastomeric (rubber-like) | N/A | N/A | N/A | N/A | N/A | N/A | * * * | N/A | * * * * * | * * * * * | |
Recommended Applications |
VisiJet® M2R-CL |
VisiJet® M2R-WT |
VisiJet® M2R-BK |
VisiJet® M2R-TN |
VisiJet® M2R-GRY |
VisiJet® M2G-CL |
VisiJet® M2G-DUR |
VisiJet® M2S-HT90 |
VisiJet® M2- EBK |
VisiJet® M2- ENT |
|
Investment Casting (Flask Method) | * * * * | * * * | * * * | * * * | * * * | * * * | N/A | * * * | N/A | N/A | |
Jigs/Fixtures/Tools | * * * * | * * * * | * * * | N/A | * * * * | * * * * * | * * * | * * * * | N/A | N/A | |
Master Patterns for RTV | * * * * | * * * * | * * * * | N/A | * * * * | * * * * | * * * | * * * * | N/A | N/A | |
General Purpose Models | * * * * * | * * * * * | * * * * * | N/A | * * * * * | * * * * * | * * * * | * * * * * | N/A | N/A | |
Functional Prototyping (snap fits) |
* * * * | * * * * | * * * | N/A | * * * * | * * * * * | * * * * * | * * * | N/A | N/A | |
Injection Molding/Direct AIM | * * * | * * * | * * * | N/A | * * * | * * * * | N/A | * * * * | N/A | N/A | |
Dental Models | N/A | N/A | N/A | * * * * * | N/A | N/A | N/A | N/A | N/A | N/A | |
Medical USP Class VI | * * * * * | * * * * * | N/A | * * * * * | * * * * * | N/A | N/A | * * * * * | N/A | N/A |