Printer Materials and Properties

F4-ELAST-BLK-10-_1-kg-Bottle-_v5-dj.jpg

The section below lists the print materials that are currently supported on the Figure 4 Standalone printer, as well as the properties of cured parts printed with these materials. Click a header to expand/collapse that material's section. Please note that not all properties in the table below apply to every material. For full technical specifications for your material, visit the Figure 4 Standalone materials page on 3dsystems.com, click the link for your material, and click the Tech Specs tab.

NOTE: All materials come in 1kg bottles.

Figure 4 TOUGH GRY 10

Metric Method Value
Color N/A Dark Gray
Description N/A Rigid, high-speed production material
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 78
Viscosity (cps @ 25C) Brookfield viscometer 493.8
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.04
Solid Density (g/cm3) ASTM D792 1.11
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 49.6
Tensile Strength @ Yield (MPa) ASTM D638 49.6
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2184
Elongation at Yield (%) ASTM D638 4
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 25
Flex Strength (MPa) ASTM D790 75.3
Flex Modulus (MPa) ASTM D790 2069
Izod Notched Impact (J/m) ASTM D256 29
Izod unnotched impact (J/m) ASTM D4812 598
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 57.9
HDT @ 66PSI (C) ASTM D648 58.6
HDT @ 264 PSI (C) ASTM D648 50.8
CTE above Tg ((μm/m)/°C) ASTM E831 165
CTE below Tg ((μm/m)/°C) ASTM E831 93
Shore D Hardness ASTM D2240 81.3
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.34
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 TOUGH GRY 15

Metric Method Value
Color N/A Gray
Description N/A Rigid production material
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method up to 41
Viscosity (cps @ 25C) Brookfield viscometer 779
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.04
Solid Density (g/cm3) ASTM D792 1.12
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 48.4
Tensile Strength @ Yield (MPa) ASTM D638 48.3
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2117
Elongation at Yield (%) ASTM D638 4
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 35
Flex Strength (MPa) ASTM D790 73
Flex Modulus (MPa) ASTM D790 1961
Izod Notched Impact (J/m) ASTM D256 32
Izod unnotched impact (J/m) ASTM D4812 599
599Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 54.6
HDT @ 66PSI (C) ASTM D648 58.8
HDT @ 264 PSI (C) ASTM D648 51.4
CTE above Tg ((μm/m)/°C) ASTM E831 158
CTE below Tg ((μm/m)/°C) ASTM E831 96
Shore D Hardness ASTM D2240 81.6
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.37
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 JCAST-GRN 10

Metric Method Value
Color N/A Gray
Description N/A Jewelry Casting
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 8
Viscosity (cps @ 25C) Brookfield viscometer 190
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.095
Solid Density (g/cm3) ASTM D792 1.18
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 13.7
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 262.4
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 12.1
Flex Strength (MPa) ASTM D790 n/a
Flex Modulus (MPa) ASTM D790 n/a
Izod Notched Impact (J/m) ASTM D256 n/a
Izod unnotched impact (J/m) ASTM D4812 n/a
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) -1.3
HDT @ 66PSI (C) ASTM D648 n/a
HDT @ 264 PSI (C) ASTM D648 n/a
CTE above Tg ((μm/m)/°C) ASTM E831 142.7
CTE below Tg ((μm/m)/°C) ASTM E831 n/a
Shore D Hardness ASTM D2240 67.5
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 1.3
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 ELAST-BLK 10

Metric Method Value
Color N/A Black
Description N/A Design Elastomeric
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 47
Viscosity (cps @ 25C) Brookfield viscometer 1201
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.06
Solid Density (g/cm3) ASTM D792 1.13
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 3.6
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 3.6
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 83
Flex Strength (MPa) ASTM D790 n/a
Flex Modulus (MPa) ASTM D790 n/a
Izod Notched Impact (J/m) ASTM D256 n/a
Izod unnotched impact (J/m) ASTM D4812 n/a
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) -26.2
HDT @ 66PSI (C) ASTM D648 n/a
HDT @ 264 PSI (C) ASTM D648 n/a
CTE above Tg ((μm/m)/°C) ASTM E831 n/a
CTE below Tg ((μm/m)/°C) ASTM E831 n/a
Shore D Hardness ASTM D2240 n/a
Shore A Hardness ASTM D2240 64.7
24 Hour water absorption (%) ASTM D570 1.4
Tear Strength (kN/m) ASTM D624 11.2

Figure 4 FLEX-BLK 10

Metric Special Considerations for FLEX-BLK 10 Method Value
Color N/A Black
Description N/A Polypropylene-like,
flexible
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 30
Viscosity (cps @ 25C) Brookfield viscometer 2108
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.06
Solid Density (g/cm3) ASTM D792 1.15
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 46
Tensile Strength @ Yield (MPa) ASTM D638 37
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 1402
Elongation at Yield (%) ASTM D638 6
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 104
Flex Strength (MPa) ASTM D790 37
Flex Modulus (MPa) ASTM D790 986
Izod Notched Impact (J/m) ASTM D256 55
Izod unnotched impact (J/m) ASTM D4812 Did not break
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 17.8
HDT @ 66PSI (C) ASTM D648 52
HDT @ 264 PSI (C) ASTM D648 43
CTE above Tg ((μm/m)/°C) ASTM E831 91
CTE below Tg ((μm/m)/°C) ASTM E831 138
Shore D Hardness ASTM D2240 76.2
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 1.4
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 MED-AMB 10

Metric Method Value
Color N/A Amber
Description N/A Translucent, Rigid Material with biocompatibility, designed to support a range of industrial and medical applications. For biocompatibility information, please visit here.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method up to 43
Viscosity (cps @ 25C) Brookfield viscometer 1138
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.12
Solid Density (g/cm3) ASTM D792 1.20
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 69
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2760
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 4
Flex Strength (MPa) ASTM D790 111
Flex Modulus (MPa) ASTM D790 2809
Izod Notched Impact (J/m) ASTM D256 18
Izod unnotched impact (J/m) ASTM D4812 220
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 109.6
HDT @ 66PSI (C) ASTM D648 118.6
HDT @ 264 PSI (C) ASTM D648 93.6
CTE above Tg ((μm/m)/°C) ASTM E831 177
CTE below Tg ((μm/m)/°C) ASTM E831 84
Shore D Hardness ASTM D2240 83.5
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.26
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 MED-WHT 10

Metric Method Value
Color N/A Ivory
Description N/A White, Rigid Material with biocompatibility, designed to support a range of industrial and medical applications. For biocompatibility information, please visit here.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 41
Viscosity (cps @ 25C) Brookfield viscometer 937
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.18
Solid Density (g/cm3) ASTM D792 1.27
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 60
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 3090
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 3
Flex Strength (MPa) ASTM D790 112
Flex Modulus (MPa) ASTM D790 3290
Izod Notched Impact (J/m) ASTM D256 17
Izod unnotched impact (J/m) ASTM D4812 91
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 102.4
HDT @ 66PSI (C) ASTM D648 102.0
HDT @ 264 PSI (C) ASTM D648 79.4
CTE above Tg ((μm/m)/°C) ASTM E831 154
CTE below Tg ((μm/m)/°C) ASTM E831 83
Shore D Hardness ASTM D2240 84.1
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.25
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 TOUGH-BLK 20

Metric Method Value
Color N/A Black
Description N/A Rigid, black plastic with industry-leading UV stability. It is ideal for high-performance, functional prototyping applications.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 45
Viscosity (cps @ 25C) Brookfield viscometer 2623
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.04
Solid Density (g/cm3) ASTM D792 1.11
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 40.4
Tensile Strength @ Yield (MPa) ASTM D638 40.4
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 1775
Elongation at Yield (%) ASTM D638 4.6
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 36
Flex Strength (MPa) ASTM D790 60.5
Flex Modulus (MPa) ASTM D790 1646
Izod Notched Impact (J/m) ASTM D256 27
Izod unnotched impact (J/m) ASTM D4812 1008
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 46
HDT @ 66PSI (C) ASTM D648 55
HDT @ 264 PSI (C) ASTM D648 45
CTE above Tg ((μm/m)/°C) ASTM E831 173
CTE below Tg ((μm/m)/°C) ASTM E831 83
Shore D Hardness ASTM D2240 78.6
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.31
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 PRO-BLK 10

Metric Method Value
Color N/A Black
Description N/A Production-grade additive manufacturing material with game-changing thermoplastic-like mechanical properties, and environmental stability of mechanical and performance properties over time.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 62
Viscosity (cps @ 25C) Brookfield viscometer 293
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.07
Solid Density (g/cm3) ASTM D792 1.16
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 63
Tensile Strength @ Yield (MPa) ASTM D638 63
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2320
Elongation at Yield (%) ASTM D638 4.7
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 12
Flex Strength (MPa) ASTM D790 92
Flex Modulus (MPa) ASTM D790 2290
Izod Notched Impact (J/m) ASTM D256 24
Izod unnotched impact (J/m) ASTM D4812 614
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 62
HDT @ 66PSI (C) ASTM D648 70
HDT @ 264 PSI (C) ASTM D648 56
CTE above Tg ((μm/m)/°C) ASTM E831 188
CTE below Tg ((μm/m)/°C) ASTM E831 71
Shore D Hardness ASTM D2240 79
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 1.16
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 HI TEMP 300-AMB

Metric Method Value
Color N/A Amber
Description N/A Industry-leading, ultra-high-temperature-resistant (HDT > 300°C), rigid plastic suitable for the harshest environments
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 36
Viscosity (cps @ 25C) Brookfield viscometer 1725
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.19
Solid Density (g/cm3) ASTM D792 1.3
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 81
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 4000
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 2.6
Flex Strength (MPa) ASTM D790 140
Flex Modulus (MPa) ASTM D790 4260
Izod Notched Impact (J/m) ASTM D256 10
Izod unnotched impact (J/m) ASTM D4812 138
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) n/a
HDT @ 66PSI (C) ASTM D648 >300
HDT @ 264 PSI (C) ASTM D648 >300
CTE above Tg ((μm/m)/°C) ASTM E831 54
CTE below Tg ((μm/m)/°C) ASTM E831 62
Shore D Hardness ASTM D2240 89
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.36
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 FLEX-BLK 20

Metric Method Value
Color N/A Black
Description N/A Flexible, high impact-resistant material for extremely durable black parts, with the look and feel of production polypropylene.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 25
Viscosity (cps @ 25C) Brookfield viscometer 2250
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.11
Solid Density (g/cm3) ASTM D792 1.18
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 36
Tensile Strength @ Yield (MPa) ASTM D638 24
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 840
Elongation at Yield (%) ASTM D638 7.5
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 86
Flex Strength (MPa) ASTM D790 22
Flex Modulus (MPa) ASTM D790 680
Izod Notched Impact (J/m) ASTM D256 91
Izod unnotched impact (J/m) ASTM D4812 Did not break
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 11
HDT @ 66PSI (C) ASTM D648 41
HDT @ 264 PSI (C) ASTM D648 <25
CTE above Tg ((μm/m)/°C) ASTM E831 188
CTE below Tg ((μm/m)/°C) ASTM E831 69
Shore D Hardness ASTM D2240 68
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.64
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 RUBBER-BLK 10

Metric Method Value
Color N/A Black
Description N/A High-tear-strength material for production-hard, rubber-like parts with slow-rebound.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 26
Viscosity (cps @ 25C) Brookfield viscometer 1413
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.11
Solid Density (g/cm3) ASTM D792 1.17
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 19
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 434
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 75
Flex Strength (MPa) ASTM D790 n/a
Flex Modulus (MPa) ASTM D790 n/a
Izod Notched Impact (J/m) ASTM D256 128
Izod unnotched impact (J/m) ASTM D4812 Did not break
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 21
HDT @ 66PSI (C) ASTM D648 n/a
HDT @ 264 PSI (C) ASTM D648 n/a
CTE above Tg ((μm/m)/°C) ASTM E831 n/a
CTE below Tg ((μm/m)/°C) ASTM E831 n/a
Shore D Hardness ASTM D2240 59
Shore A Hardness ASTM D2240 97
24 Hour water absorption (%) ASTM D570 0.4
Tear Strength (kN/m) ASTM D624 76

Figure 4 EGGSHELL-AMB 10

Metric Method Value
Color N/A Amber
Description N/A Rigid plastic used to create sacrificial tooling that withstands silicone injection at high temperature and pressure, but breaks away easily
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 43
Viscosity (cps @ 25C) Brookfield viscometer 212
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.08
Solid Density (g/cm3) ASTM D792 1.16
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 72
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2765
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 5
Flex Strength (MPa) ASTM D790 114
Flex Modulus (MPa) ASTM D790 2890
Izod Notched Impact (J/m) ASTM D256 15
Izod unnotched impact (J/m) ASTM D4812 138
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 83
HDT @ 66PSI (C) ASTM D648 89
HDT @ 264 PSI (C) ASTM D648 72
CTE above Tg ((μm/m)/°C) ASTM E831 n/a
CTE below Tg ((μm/m)/°C) ASTM E831 n/a
Shore D Hardness ASTM D2240 85
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.27
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 RUBBER-65A BLK

Metric Method Value
Color N/A Black
Description N/A A mid-tear strength, production-grade rubber combined with Shore 65A hardness and a high elongation at break
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 15
Viscosity (cps @ 25C) Brookfield viscometer 240
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.03
Solid Density (g/cm3) ASTM D792 1.12
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 5
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 23
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 126
Flex Strength (MPa) ASTM D790 n/a
Flex Modulus (MPa) ASTM D790 n/a
Izod Notched Impact (J/m) ASTM D256 n/a
Izod unnotched impact (J/m) ASTM D4812 n/a
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) -10
HDT @ 66PSI (C) ASTM D648 n/a
HDT @ 264 PSI (C) ASTM D648 n/a
CTE above Tg ((μm/m)/°C) ASTM E831 184
CTE below Tg ((μm/m)/°C) ASTM E831 84
Shore D Hardness ASTM D2240 n/a
Shore A Hardness ASTM D2240 65
24 Hour water absorption (%) ASTM D570 2.6
Tear Strength (kN/m) ASTM D624 1.8

Figure 4 JEWEL MASTER GRY

Metric Method Value
Color N/A Gray
Description N/A A versatile, high HDT master pattern material for jewelry silicone molds and high-visualization detailed prototypes of complex and fine designs.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 14
Viscosity (cps @ 25C) Brookfield viscometer 2147
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.19
Solid Density (g/cm3) ASTM D792 1.29
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 67
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 3548
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 2.5
Flex Strength (MPa) ASTM D790 129
Flex Modulus (MPa) ASTM D790 3980
Izod Notched Impact (J/m) ASTM D256 n/a
Izod unnotched impact (J/m) ASTM D4812 n/a
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) n/a
HDT @ 66PSI (C) ASTM D648 >300
HDT @ 264 PSI (C) ASTM D648 111
CTE above Tg ((μm/m)/°C) ASTM E831 146
CTE below Tg ((μm/m)/°C) ASTM E831 80
Shore D Hardness ASTM D2240 88
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 n/a
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 Rigid White

Metric Method Value
Color N/A White
Description N/A Opaque rigid white production-grade plastic for same-day parts. This biocompatible-capable material
provides a smooth surface finish, long-term environmental stability, and long-lasting, clean white color.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 47
Viscosity (cps @ 25C) Brookfield viscometer 270
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.09
Solid Density (g/cm3) ASTM D792 1.16
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 57
Tensile Strength @ Yield (MPa) ASTM D638 57
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2100
Elongation at Yield (%) ASTM D638 4.5
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 20
Flex Strength (MPa) ASTM D790 84
Flex Modulus (MPa) ASTM D790 2200
Izod Notched Impact (J/m) ASTM D256 21
Izod unnotched impact (J/m) ASTM D4812 160
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 64
HDT @ 66PSI (C) ASTM D648 65
HDT @ 264 PSI (C) ASTM D648 55
CTE above Tg ((μm/m)/°C) ASTM E831 146
CTE below Tg ((μm/m)/°C) ASTM E831 82
Shore D Hardness ASTM D2240 81
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 1.88
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 High Temp 150C FR Black

Metric Method Value
Color N/A Black
Description N/A A rigid, fire-retardant resin that can be used for production of parts requiring UL 94 V0 capability as well as FAR Part 23.853 and FAR 25.853 capability
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 36
Viscosity (cps @ 25C) Brookfield viscometer 1700
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.2
Solid Density (g/cm3) ASTM D792 1.29
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 58
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2600
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 4
Flex Strength (MPa) ASTM D790 100
Flex Modulus (MPa) ASTM D790 2900
Izod Notched Impact (J/m) ASTM D256 10
Izod unnotched impact (J/m) ASTM D4812 50
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) n/a
HDT @ 66PSI (C) ASTM D648 >150
HDT @ 264 PSI (C) ASTM D648 89
CTE above Tg ((μm/m)/°C) ASTM E831 158
CTE below Tg ((μm/m)/°C) ASTM E831 98
Shore D Hardness ASTM D2240 85
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.26
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 Rigid Gray

Metric Method Value
Color N/A Gray
Description N/A The balance of thermal and mechanical properties, combined with excellent print quality and long-term Indoor and outdoor stability for prototyping and production.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 48
Viscosity (cps @ 25C) Brookfield viscometer 300
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.07
Solid Density (g/cm3) ASTM D792 1.15
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 61
Tensile Strength @ Yield (MPa) ASTM D638 61
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2400
Elongation at Yield (%) ASTM D638 4.6
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 30
Flex Strength (MPa) ASTM D790 87
Flex Modulus (MPa) ASTM D790 2200
Izod Notched Impact (J/m) ASTM D256 21
Izod unnotched impact (J/m) ASTM D4812 150
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 60
HDT @ 66PSI (C) ASTM D648 72
HDT @ 264 PSI (C) ASTM D648 59
CTE above Tg ((μm/m)/°C) ASTM E831 166
CTE below Tg ((μm/m)/°C) ASTM E831 81
Shore D Hardness ASTM D2240 82
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.99
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 Tough 60C White

Metric Method Value
Color N/A White
Description N/A Versatile utilities with a good combination of impact strength, elongation, and tensile strength. Long-term indoor and outdoor mechanical and color stability.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 24
Viscosity (cps @ 25C) Brookfield viscometer 1800
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.15
Solid Density (g/cm3) ASTM D792 1.23
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 35
Tensile Strength @ Yield (MPa) ASTM D638 35
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 1500
Elongation at Yield (%) ASTM D638 7.1
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 23
Flex Strength (MPa) ASTM D790 52
Flex Modulus (MPa) ASTM D790 1500
Izod Notched Impact (J/m) ASTM D256 34
Izod unnotched impact (J/m) ASTM D4812 90
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 50
HDT @ 66PSI (C) ASTM D648 65
HDT @ 264 PSI (C) ASTM D648 48
CTE above Tg ((μm/m)/°C) ASTM E831 171
CTE below Tg ((μm/m)/°C) ASTM E831 95
Shore D Hardness ASTM D2240 79
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.61
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 Tough 65C Black

Metric Method Value
Color N/A Black
Description N/A Versatile utilities with a good combination of impact strength, elongation, and tensile strength. Long-term Indoor and Outdoor environmental stability.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 30
Viscosity (cps @ 25C) Brookfield viscometer 1900
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.13
Solid Density (g/cm3) ASTM D792 1.22
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 41
Tensile Strength @ Yield (MPa) ASTM D638 40
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 1700
Elongation at Yield (%) ASTM D638 6.6
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 35
Flex Strength (MPa) ASTM D790 55
Flex Modulus (MPa) ASTM D790 1600
Izod Notched Impact (J/m) ASTM D256 31
Izod unnotched impact (J/m) ASTM D4812 100
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 50
HDT @ 66PSI (C) ASTM D648 70
HDT @ 264 PSI (C) ASTM D648 51
CTE above Tg ((μm/m)/°C) ASTM E831 163
CTE below Tg ((μm/m)/°C) ASTM E831 92
Shore D Hardness ASTM D2240 81
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 0.62
Tear Strength (kN/m) ASTM D624 n/a

Figure 4 Rigid 140C Black

Metric Method Value
Color N/A Black
Description N/A A high performance material, delivering production-grade parts with long-term mechanical stability in various environments. Suitable for housings, casings, and all types of prototyping or production components. Ideal for automotive under-the-hood and internal cabin end-use clips, covers, connectors, housings & fasteners, electrical latching, and board connectors.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal Method Up to 25
Viscosity (cps @ 25C) Brookfield viscometer 900
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.16
Solid Density (g/cm3) ASTM D792 1.19
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer/rubber) 80
Tensile Strength @ Yield (MPa) ASTM D638 n/a
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2800
Elongation at Yield (%) ASTM D638 n/a
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 5.6
Flex Strength (MPa) ASTM D790 110
Flex Modulus (MPa) ASTM D790 2700
Izod Notched Impact (J/m) ASTM D256 16
Izod unnotched impact (J/m) ASTM D4812 330
Tg (DMA, E") ASTM E1640 (E"at 1°C/min) 124
HDT @ 66PSI (C) ASTM D648 140
HDT @ 264 PSI (C) ASTM D648 124
CTE above Tg ((μm/m)/°C) ASTM E831 110
CTE below Tg ((μm/m)/°C) ASTM E831 89
Shore D Hardness ASTM D2240 84
Shore A Hardness ASTM D2240 n/a
24 Hour water absorption (%) ASTM D570 1.54
Tear Strength (kN/m) ASTM D624 n/a