Print Material Bottles

F4-ELAST-BLK-10-_1-kg-Bottle-_v5-dj.jpg

The table below lists the print materials that are currently supported on the Figure 4 Standalone printer, as well as the properties of cured parts printed with these materials. Please note that not all properties in the table below apply to every material. As such, different materials will have blank spaces for some of the property fields below.

 

NOTE: All materials come in 1kg bottles.

 

Metric Method Figure 4 TOUGH GRY 10 Figure 4 TOUGH GRY 15 Figure 4 JCAST-GRN 10 Figure 4 ELAST-BLK 10 Figure 4 FLEX-BLK 10

Please see Special Considerations for FLEX BLK 10

Figure 4 MED-AMB 10 Figure 4 MED-WHT 10 Figure 4 TOUGH-BLK 20
Color N/A Dark Gray Gray Green Black Black Amber Ivory Black
Description N/A Rigid, high-speed production material

Rigid production material

Jewelry Casting Design Elastomeric Polypropylene-like,
flexible
Translucent, Rigid Material with biocompatibility, designed to support a range of industrial and medical applications. For biocompatibility information, please visit here. White, Rigid Material with biocompatibility, designed to support a range of industrial and medical applications. For biocompatibility information, please visit here. Rigid, black plastic with industry-leading UV stability. It is ideal for high-performance, functional prototyping applications.
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style Internal method up to 78 up to 41 up to 8 up to 47 up to 30 up to 43 up to 41 up to 45
Viscosity (cps @ 25C) Brookfield viscometer 493.8 779 190 1201 2108 1138 937 2623
Liquid Density (g/cm3) Kruss K11 Force Tensiometer 1.04 1.04 1.095 1.06 1.06 1.12 1.18 1.04
Solid Density (g/cm3) ASTM D792 1.11 1.12 1.18 1.13 1.15 1.20 1.27 1.11
Tensile Strength Ultimate (MPa) ASTM D638 (rigid)/D412(elastomer) 49.6 48.4 13.7 3.6 46 69 60 40.4
Tensile Strength @ Yield (MPa) ASTM D638 49.6 48.3     37     40.4
Tensile Modulus (MPa) ASTM D638 (rigid)/D412 (elastomer) 2184 2117 262.4 3.6 1402 2760 3090 1775
Elongation at Yield (%) ASTM D638 4 4     6     4.6
Elongation at Break (%) ASTM D638 (rigid)/D412(elastomer) 25 35 12.1 83 104 4 3 36
Flex Strength (MPa) ASTM D790 75.3 73     37 111 112 60.5
Flex Modulus (MPa) ASTM D790 2069 1961     986 2809 3290 1646
Izod Notched Impact (J/m) ASTM D256 29 32     55 18 17 27
Izod unnotched impact (J/m) ASTM D4812 598 599     Did not break 220 91 1008
Tg (DMA, E") ASTM E1640 (E"at 1C/min) 57.9 54.6 -1.3 -26.2 17.8 109.6 102.4 46
HDT @ 66PSI (C) ASTM D648 58.6 58.8     52 118.6 102.0 55
HDT @ 264 PSI (C) ASTM D648 50.8 51.4     43 93.6 79.4 45
CTE above Tg ((μm/m)/°C) ASTM E831 165 158 142.7   91 177 154 173
CTE below Tg ((μm/m)/°C) ASTM E831 93 96     138 84 83 83
Shore D Hardness ASTM D2240 81.3 81.6 67.5   76.2 83.5 84.1 78.6
Shore A Hardness ASTM D2240       64.7        
24 Hour water absorption (%) ASTM D570 0.34 0.37 1.3 1.4 1.4 0.26 0.25 0.31
Tear Strength (kN/m) ASTM D624       11.2