The table below lists the Figure 4 materials that are currently supported on the Figure 4 Modular system, as well as the properties of cured parts printed with these materials. Please note that not all properties in the table below apply to every material. As such, different materials will have blank spaces for some of the property fields below. New materials are added to the material library from time to time. Please check the Customer Information Bulletins page for the latest updates.
NOTE: Materials come in 2.5kg cartridges. |
NOTE: If you wish to print this page, scroll to the bottom of this page and click the "printer friendly version" link. On the page in the new tab, press ctrl+P (cmd+P on Mac) to print the document or save it as a PDF. Print/save in landscape orientation and 50% scale for best results to print the full chart. |
If you cannot see your material:
Scroll or swipe to the right.
Metric | Method | Figure 4 TOUGH GRY 10 | Figure 4 TOUGH GRY 15 | Figure 4 ELAST-BLK 10 | Figure 4 FLEX-BLK 10
Please see Special Considerations for FLEX-BLK 10 |
Figure 4 MED-AMB 10 | Figure 4 MED-WHT 10 | Figure 4 TOUGH-BLK 20 | Figure 4 PRO-BLK 10 | Figure 4 HI TEMP 300-AMB | Figure 4 FLEX-BLK 20 | Figure 4 RUBBER-BLK 10 |
Figure 4 EGGSHELL-AMB 10 | Figure 4 RUBBER-65A BLK | Figure 4 Rigid White | Figure 4 High Temp 150C FR Black | Figure 4 Rigid Gray |
Figure 4 Tough 60C White | Figure 4 Tough 65C Black |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Color | N/A | Dark Gray | Gray | Black | Black | Amber | Ivory | Black | Black | Amber | Black | Black | Amber | Black | White | Black | Gray | White | Black |
Description | N/A | Rigid, high-speed production material |
Rigid production material |
Design Elastomeric | Polypropylene-like, flexible |
Translucent, Rigid Material with biocompatibility, designed to support a range of industrial and medical applications. For biocompatibility information, please visit here. | White, Rigid Material with biocompatibility, designed to support a range of industrial and medical applications. For biocompatibility information, please visit here. | Rigid, black plastic with industry-leading UV stability. It is ideal for high-performance, functional prototyping applications. | Production-grade additive manufacturing material with game-changing thermoplastic-like mechanical properties, and environmental stability of mechanical and performance properties over time. | Industry-leading, ultra-high-temperature-resistant (HDT > 300°C), rigid plastic suitable for the harshest environments | Flexible, high impact-resistant material for extremely durable black parts, with the look and feel of production polypropylene. | High-tear-strength material for production-hard, rubber-like parts with slow-rebound. | Rigid plastic used to create sacrificial tooling that withstands silicone injection at high temperature and pressure, but breaks away easily | A mid-tear strength, production-grade rubber combined with Shore 65A hardness and a high elongation at break | Opaque rigid white production-grade plastic for same-day parts. This biocompatible-capable material provides a smooth surface finish, long-term environmental stability, and long-lasting, clean white color. |
A rigid, fire-retardant resin that can be used for production of parts requiring UL 94 V0 capability as well as FAR Part 23.853 and FAR 25.853 capability | The balance of thermal and mechanical properties, combined with excellent print quality and long-term Indoor and outdoor stability for prototyping and production. | Versatile utilities with a good combination of impact strength, elongation, and tensile strength. Long-term indoor and outdoor mechanical and color stability. | Versatile utilities with a good combination of impact strength, elongation, and tensile strength. Long-term Indoor and Outdoor environmental stability. |
Speed (mm/hr) - 50 µm Print Mode/Standard Build Style | Internal method | up to 78 | up to 41 | up to 47 | up to 30 | up to 43 | up to 41 | up to 45 | up to 62 | up to 36 | up to 25 | up to 26 | up to 43 | up to 15 | up to 47 | up to 36 | up to 48 | up to 24 | up to 30 |
Viscosity (cps @ 25C) | Brookfield viscometer | 493.8 | 779 | 1201 | 2108 | 1138 | 937 | 2623 | 293 | 1725 | 2250 | 1413 | 212 | 240 | 270 | 1700 | 300 | 1800 | 1900 |
Liquid Density (g/cm3) | Kruss K11 Force Tensiometer | 1.04 | 1.04 | 1.06 | 1.06 | 1.12 | 1.18 | 1.04 | 1.07 | 1.19 | 1.11 | 1.11 | 1.08 | 1.03 | 1.09 | 1.2 | 1.07 | 1.15 | 1.13 |
Solid Density (g/cm3) | ASTM D792 | 1.11 | 1.12 | 1.13 | 1.15 | 1.20 | 1.27 | 1.11 | 1.16 | 1.3 | 1.18 | 1.17 | 1.16 | 1.12 | 1.16 | 1.29 | 1.15 | 1.23 | 1.22 |
Tensile Strength Ultimate (MPa) | ASTM D638 (rigid)/D412(elastomer/rubber) | 49.6 | 48.4 | 3.6 | 46 | 69 | 60 | 40.4 | 63 | 81 | 36 | 19 | 72 | 5 | 57 | 58 | 61 | 35 | 41 |
Tensile Strength @ Yield (MPa) | ASTM D638 | 49.6 | 48.3 | 37 | 40.4 | 63 | 24 | 57 | 61 | 35 | 40 | ||||||||
Tensile Modulus (MPa) | ASTM D638 (rigid)/D412 (elastomer) | 2184 | 2117 | 3.6 | 1402 | 2760 | 3090 | 1775 | 2320 | 4000 | 840 | 434 | 2765 | 23 | 2100 | 2600 | 2400 | 1500 | 1700 |
Elongation at Yield (%) | ASTM D638 | 4 | 4 | 6 | 4.6 | 4.7 | 7.5 | 4.5 | 4.6 | 7.1 | 6.6 | ||||||||
Elongation at Break (%) | ASTM D638 (rigid)/D412(elastomer) | 25 | 35 | 83 | 104 | 4 | 3 | 36 | 12 | 2.6 | 86 | 75 | 5 | 126 | 20 | 4 | 30 | 23 | 35 |
Flex Strength (MPa) | ASTM D790 | 75.3 | 73 | 37 | 111 | 112 | 60.5 | 92 | 140 | 22 | 114 | 84 | 100 | 87 | 52 | 55 | |||
Flex Modulus (MPa) | ASTM D790 | 2069 | 1961 | 986 | 2809 | 3290 | 1646 | 2290 | 4260 | 680 | 2890 | 2200 | 2900 | 2200 | 1500 | 1600 | |||
Izod Notched Impact (J/m) | ASTM D256 | 29 | 32 | 55 | 18 | 17 | 27 | 24 | 10 | 91 | 128 | 15 | 21 | 10 | 21 | 34 | 31 | ||
Izod unnotched impact (J/m) | ASTM D4812 | 598 | 599 | Did not break | 220 | 91 | 1008 | 614 | 138 | Did not break | Did not break | 138 | 160 | 50 | 150 | 90 | 100 | ||
Tg (DMA, E") | ASTM E1640 (E"at 1°C/min) | 57.9 | 54.6 | -26.2 | 17.8 | 109.6 | 102.4 | 46 | 62 | 11 | 21 | 83 | -10 | 64 | 60 | 50 | 50 | ||
HDT @ 66PSI (C) | ASTM D648 | 58.6 | 58.8 | 52 | 118.6 | 102.0 | 55 | 70 | >300 | 41 | 89 | 65 | >150 | 72 | 65 | 70 | |||
HDT @ 264 PSI (C) | ASTM D648 | 50.8 | 51.4 | 43 | 93.6 | 79.4 | 45 | 56 | >300 | <25 | 72 | 55 | 89 | 59 | 48 | 51 | |||
CTE above Tg ((μm/m)/°C) | ASTM E831 | 165 | 158 | 91 | 177 | 154 | 173 | 188 | 54 | 188 | 184 | 146 | 158 | 166 | 171 | 163 | |||
CTE below Tg ((μm/m)/°C) | ASTM E831 | 93 | 96 | 138 | 84 | 83 | 83 | 71 | 62 | 69 | 84 | 82 | 98 | 81 | 95 | 92 | |||
Shore D Hardness | ASTM D2240 | 81.3 | 81.6 | 76.2 | 83.5 | 84.1 | 78.6 | 79 | 89 | 68 | 59 | 85 | 81 | 85 | 82 | 79 | 81 | ||
Shore A Hardness | ASTM D2240 | 64.7 | 97 | 65 | |||||||||||||||
24 Hour water absorption (%) | ASTM D570 | 0.34 | 0.37 | 1.4 | 1.4 | 0.26 | 0.25 | 0.31 | 1.16 | 0.36 | 0.64 | 0.4 | 0.27 | 2.6 | 1.88 | 0.26 | 0.99 | 0.61 | 0.62 |
Tear Strength (kN/m) | ASTM D624 | 11.2 | 76 | 1.8 |