Print Settings

Print Settings allow you to set the parameters of your print and build them into your print file. There are four (4) different options for setting the print parameters.

Presets
  • Draft - A print that does not require strength or fine details
  • Standard - A strong print that does not require fine details
  • Premium - A strong print that requires fine details
  • Custom - Allows you to set the layer thickness, density and fill pattern. You may also enable or disable supports and rafts.
Layer Resolution
  • 0.070 mm - High quality prints
  • 0.200 mm - Shorter print time
Density
  • Hollow - Short print times and low material use
  • Strong - Stronger prints
  • Almost Solid - High material use and almost solid prints
Fill Pattern
  • Honeycomb - Used for strong prints
  • Diamonds - For general printing
  • Lines - Shorter print times

Print Settings - Draft

Select Draft for prints that do not require strength or fine detail.

Layers:  0.200 mm
Density: Hollow
Fill Pattern: Lines

Print Settings - Standard

Select Standard for strong prints that do not require fine detail.

Layers:  0.200 mm
Density:  Strong
Fill Pattern:  Diamonds

Print Settings - Premium

Layers:  0.070 mm
Density:  Strong
Fill Pattern:  Diamonds

Print Settings - Custom

Select Custom to view the current print settings. You can personalize the settings by selecting a category and then selecting the arrows to expand your options.

Layers:
  • 0.070 mm
  • 0.200 mm
Density:
  • Hollow
  • Strong
  • Almost Solid
Fill Pattern:
  • Honeycomb
  • Diamonds
  • Lines

Sidewalks

Sidewalks (A) are mesh boundaries that print around the outside diameter of a part. Its main purpose is to reduce the tendency of warping especially when printing flat parts with ABS material. They should not be used for parts that have fine details.

Supports

Supports are used when printing creations that need a supporting structure to print properly. These parts may have overhangs, cavities or other openings that will not print correctly without a supporting structure.