Part Properties after UV Post-cure

The table below shows the mechanical properties from each cure unit.

Solid Material

Metric ASTM Method LC-3D ProCure 350 ProCure 750
Max Part Size L x W x H Ø260 x 195mm 350 x 350 x 350mm 630 x 1050 x 1050mm
Tensile Strength Ultimate ASTM D638 Type IV 52 MPa 42 MPa 50 MPa
Tensile Strength at Yield ASTM D638 Type IV 52 MPa 42 MPa 50 MPa
Tensile Modulus ASTM D638 Type IV 2100 MPa 1900 MPa 2100 MPa
Elongation at Break ASTM D638 Type IV 24% 41% 34%
Elongation at Yield ASTM D638 Type IV 4.5% 4.4% 4.5%
Flex Strength ASTM D790 88 MPa 39 MPa 66 MPa
Flex Modulus ASTM D790 2300 MPa 1600 MPa 1800 MPa
Izod Notched Impact ASTM D256 23 J/m 34 J/m 24 J/m
Izod Unnotched Impact ASTM D4812 170 J/m 205 J/m 198 J/m
Shore Hardness ASTM D2240 80 D 79 D 80 D
HDT 0.455MPa/66PSI ASTM D648 64 C 56 C  58 C
HDT 1.82MPa/264PSI ASTM D648 52 C 48 C 49 C

The performance characteristics of these products may differ according to variations in printing and post processing conditions, test equipment, product application, operating conditions, or with end use. 3D Systems makes no warranties of any type, express or implied, including, but not limited to, the warranties of merchantability or fitness for a particular use.